NEYRA CORPORATION TARCONITE COAL TAR PAVEMENT SEALER
- Prevents Oxidation: Neyra Tarconite driveway sealer shields against the drying action of the sun. Reduces raveling, cracking, and deterioration.
- Jet Black Color: Tarconite restores that clean, new look.
- Longer Lasting: High solids enhance suspension of mineral aggregate to provide a smooth, even-wearing surface.
- Highly Resistant: Neyra Tarconite driveway sealer resists gasoline, oils, acids, and jet fuel.
- Fortified Formula: Tarconite is modified with ingredients that give it superior water resistance and significantly improve its adhesion to the pavement
Tarconite provides up to 50% greater wear than non-fortified sealers, making it ideal for high-traffic areas, while protecting for pennies a square foot, preventing costly repairs. Tarconite also meets and exceeds rigorous FAA requirements for airport pavements and meets Government and ASTM Specifications.
FASS-DRI™
Featuring Advanced NANO-CURE Technology. Dramatically reduces curing time of both Coal Tar and Asphalt Based Sealers.
- 1: Toughness, Adhesion, Flexibility, Color, Sand Suspension
- 2: Reduces tracking and power steering marks, locks in sand and makes coating dry blacker
- 3: Improves sand suspension and uniform distribution of sand slurry mixes
This pavement sealer additive is the result of an exciting break-through in NANO-CURE chemistry. FASS-DRI™ additive enables you to open a parking lot to traffic in as little as 6 hours.
CRACKMASTER™ SUPREME DF
THE finest hot applied crackfilling material. Designed for use in both direct fire and oil-jacketed kettles. Ideal for all crack filling applications.
- Description: CrackMaster™ Supreme is a single component, hot-applied, rubberized asphalt crack and joint sealant. CrackMaster™ Supreme is specially formulated for both direct fire and oil-jacketed melters. It is heat stabilized to withstand temperatures up to 450°F without experiencing polymer degredation. When melted and properly applied it forms a resilient crack sealant for both asphaltic and cementatious pavements. CrackMaster™ Supreme meets manufacturer’s specifications.
- Uses: CrackMaster™ Supreme is designed to seal expansion joints, longitudinal and transverse cracks, joints between concrete and asphalt shoulders, and random cracks in both asphalt and concrete pavements. CrackMaster™ Supreme is relatively hard and has a high softening point, which makes it well suited for parking lots and driveways.
- Application: Apply heated CrackMaster™ Supreme using either a pump and wand system or a pour pot. For best results the sealant depth to width ratio should not exceed 2 to 1 (i.e. 2-inches deep to 1-inch wide).
- Clean Up: Wash tools in water before material dries.
PREP SEAL™ – READY TO USE OIL SPOT PRIMER
THE finest hot applied crackfilling material. Designed for use in both direct fire and oil-jacketed kettles. Ideal for all crack filling applications.
- Description: A ready to use polymer based emulsion designed to seal oil, grease, and gasoline spots or stain prior to the application of pavement sealers over asphalt surfaces.
- Surface Preparation: Scrape, wire brush, or burn off excessive build-up of oil, grease, and gasoline.
- Mixing Procedures: Stir thoroughly. DO NOT DILUTE.
- Application: Apply with brush, roller or spray. Allow Prep Seal to dry completely before applying pavement sealer.
- Clean Up: Wash tools in water before material dries.
- IMPORTANT: Temperatures must be above 50°F both during application and for a period of at least 24 hours after application. Do not apply when rain is imminent or forecast.